LX three-component Super-smooth High resilience Silicone oil finishing agent

The product is suitable for polyester two-dimensional, three-dimensional crimped fibers finishing, a mesh block copolymer polyol-modified silicone finishing agent, with a variety of reactive groups, using a variety of ultra-high molecular polymer and efficiency surfactants complex can be given a special fiber smooth, stiff and full handle.

1, Uses

1) using the object: After suitable hollow polyester staple fiber finishing, fibers play a smooth, stiff action and high resilience.

2) Features and Benefits:

(1) forming a reticular chemistry of a surface coating of good fiber

(2) excellent smooth, stiff feel, fully resilient reinforcing fibers

(3) a good penetration into the interior of the fibers so that the fiber becomes smooth, stiff

(4) green-aids, free of APEO, NPEO, in line with European ROHS environmental standards

3) for the ratio

1707:1708:1709 = 8.5:2.5:0.3

2, Performance characteristic table

Name

1707

1708

1709

Appearance

White emulsion

White emulsion

colorless transparent liquid

Assay

38% ± 2

35% ± 2

≥96%

Ph value

9-10

7-8

11 to 12

3. The method of preparation:

1) two-dimensional method of bath ingredients

(1) Padding bath tank (as 113kg Silicone oil dope, 1000kg water, for example):

(A) Silicone oil in a clean bucket, the 1709 material 3kg 30kg of water was added, stirred for 10 minutes and put away into the water ahead of the half padding bath tank

(B) the 1707 feed 85 kg, 1708 with 25 kg feed tank bath, stir

(C) the remaining water was added to the bath, mix use padding

(2) spray formulation bath method (with a three-dimensional manner bath ingredients)

(3) additional liquid ingredients manner (as 11.3kg Silicone oil liquid, 50kg water, for example)

(A) The 1709 material was added 0.3 kg 30kg of water, stirred for 10 minutes

(B) the 1707 feed 8.5 kg, 1708 with 2.5 kg material into the sump with stirring for 10 minutes

(C) the remaining 20 kg of water was added with stirring sump evenly additional use

2) a three-dimensional manner bath ingredients (as 11.3kg Silicone oil dope, 100kg water, for example)

(1) The 1709 material was added 0.3 kg 30kg of water, stirred for 10 minutes

(2) the 1707 feed 8.5 kg, 1708 feed 2.5 kg with bath tank, stirred for 10 minutes

(3) the remaining 70 kg of water were added to stir the bath to use the shower

4, Post-weaving Silicone oil fueling conditions:

1) the location and method of supply

D Best Fuel method:

Padding: will "padding bath tank dosing method" with a good bath directly at a certain time (according to the wire handle the situation and requirements), supplemented by "additional liquid dosing method" with a good bath.

Spray: Spray directly after crimping machine according to "three-dimensional manner ingredients bath" with a good bath.

D Best Fuel method:

Spray: Spray directly after crimping machine according to "three-dimensional manner ingredients bath" with a good bath.

2) oven temperature:

[A] preheating zone area: 140 ℃ 
[II] drying zone: 170 ~ 190 ℃, the highest not be greater than 210 ℃ 
District cooling zone [three]: 140 ℃

3) optimum fiber oiling rate of 0.3% to 0.4% by weight, per ton of fiber used Silicone oil 8kg ~ 10kg.

5, Cautions

1) This product has good compatibility with cationic and non - ionic , can not be used with anionic.2) The product should be stored in clean, sealed plastic or steel drum, shelf life is six months.