LX-12 suoer stiff, smooth Silicone oil finishing agent

The product is a polyester two-dimensional, three-dimensional crimped fibers silicone finishing agent, using a variety of ultra-high molecular polymers with efficient surfactants complex, with a variety of reactive groups can be given fiber suoer stiff, smooth and plump feel.

1, Uses

1) using the object: After suitable hollow polyester staple fiber finishing, fiber plays the role of smooth and high resilience.

2) Effective Ingredients: 40%

3) Features and Benefits:

(1) forming a reticular chemistry of a surface coating of good fiber

(2) excellent stiff, smooth feel, full of fiber reinforced resilience

(3) a good penetration into the interior of the fibers so that the fiber becomes stiff, smooth

(4) green-aids, free of APEO, in line with European ROHS environmental standards

3) for the ratio

A:B:C:D = 7:2:1:0.35

2, Performance characteristic table

Name

A

B

C

D

Appearance

White emulsion

White emulsion

colorless transparent liquid

colorless transparent liquid

Assay

38% ± 2

45% ± 2

12% ± 2

≥96%

Ph value

9-10

7-8

4-5

7

3. The method of preparation:

1) two-dimensional method of bath ingredients

(1) Padding bath tank (as 103.5kg Silicone oil dope, 1000kg water, for example):

(A) Silicone oil in a clean bucket, the Charge D was added 3.5 kg 30kg of water, stirred for 10 minutes and put away into the water ahead of the half padding bath tank

(B) A material 70 kg, B material 20 kg with bath tank, stir

(C) the remaining water was added to the bath, add 10 kg C material Stir to use padding

(2) spray formulation bath method (with a three-dimensional manner bath ingredients)

(3) additional liquid ingredients manner (as 10.35kg Silicone oil liquid, 50kg water, for example)

(A) D is 30kg feed 0.35 kg of water was added, stirred for 10 minutes

(B) A material 7 kg, B 2 kg with the material with oil bath, stirring for 10 minutes

(C) the remaining 20 kg of water was added with sump Stir, add C 1 kg feed supplemented with stirring for 5 minutes use

2) a three-dimensional manner bath ingredients (as 10.35kg Silicone oil dope, 100kg water, for example)

(1) D is 30kg feed 0.35 kg of water was added, stirred for 10 minutes

(2) A material 7 kg, B 2 kg feed with bathing tank, stirred for 10 minutes 
(3) The remaining 70 kg water was added to the bath Stir, add C 1 kg material was stirred for 5 minutes using a spray

4, Post-weaving Silicone oil fueling conditions:

1) the location and method of supply

D Best Fuel method:

Padding: will "padding bath tank dosing method" with a good bath directly at a certain time (according to the wire handle situations and requirements), supplemented by "additional liquid dosing method" with good bath.

Spray: Spray directly after crimping machine according to "three-dimensional manner ingredients bath" with a good bath.

D Best Fuel method:

Spray: Spray directly after crimping machine according to "three-dimensional manner ingredients bath" with a good bath.

2) oven temperature:

[A] preheating zone area: 140 ℃ 
[II] drying zone: 170 ~ 190 ℃, the highest not be greater than 210 ℃ 
District cooling zone [three]: 140 ℃

3) optimum fiber oiling rate of 0.3% to 0.4% by weight, per ton of fiber used Silicone oil 8kg ~ 10kg.

5, Cautions

1) This product has good compatibility with cationic and non - ionic , can not be used with anionic.

2) The product should be stored in clean, sealed plastic or steel drum, shelf life is six months.